2.) An S-five ninety alloy specimen nine hundred mm long will be subjected to eighty MPa tensile stress at eight hundred and fifteen degrees celcius. Later after five thousand of hours, compute its elongation. Consider a sum of one point five mm in the both immediate and main creep elongations.

2.) An S-five ninety alloy specimen nine hundred mm long will be subjected to eighty MPa tensile stress at eight hundred and fifteen degrees celcius. Later after five thousand of hours, compute its elongation. Consider a sum of one point five mm in the both immediate and main creep elongations.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A 2.0-inch diameter 4140 steel bar is austenized and tempered in oil without Agitation, determine the resulting hardness at 0.6 inches below the surface, present all the Procedure to arrive at the answer (include sketch of the piece and graph used with steps Using word forms)
Sorry I forgot to add the table. I think the answers will change this time The following creep data were taken on an aluminum alloy at 480 C (900 F) and a constant stress of 2.75 MPa (400 psi). Plot the data as strain versus time, a) then determine the steady-state or minimum creep rate. Note: The initial and instantaneous strain is not included. b) Identify at what time can a secondary creep region occur and at what time would it end to start the tertiary region in a creep curve: (see attachment).
The following creep data were taken on an aluminum alloy at 480 C (900 F) and a constant stress of 2.75 MPa (400 psi). Plot the data as strain versus time, a) then determine the steady-state or minimum creep rate. Note: The initial and instantaneous strain is not included. b) Identify at what time can a secondary creep region occur and at what time would it end to start the tertiary region in a creep curve: (see attachment).
O The following engineering stress-strain data were obtained for a 0.2% C plain-carbon steel. (i) Plot the engineering stress-strain curve. (ii) Determine the ultimate tensile strength of the alloy. (iii) Determine the percent elongation at fracture. Engineering Engineering Engineering Engineering Stress Strain Stress Strain (ksi) (in./in.) (ksi) (in./in.) 76 0.08 30 0.001 75 0.10 55 0.002 73 0.12 60 0.005 69 0.14 68 0.010 65 0.16 72 0.020 56 0.18 74 0.040 51 0.19 75 0.060 (Fracture)
Two cylindrical specimens of an alloy are to be strain hardened by reducing their cross- sectional areas. for one specimen. the initial and deformedradii are 17 mm and 12 mm, respectively. The second specimen. with an initial radius of 13 mm, must have the same deformed hardness as the firstspecimen What is the second specimen's radius affer deformation”
6. The following engineering stress-strain data were obtained for 0.2% C plain carbon steel. (a) Plot the engineering stress-strain curve (b) Determine the ultimate tensile strength for the alloy (c) Determine the percent elongation at fracture (d) Plot the true stress-strain curve Engineering strain, in./in. Engineering stress, ksi 30 0.001 55 0.002 60 0.005 68 0.01 72 0.02 74 0.04 75 0.06 76 0.08 75 0.1 73 0.12 69 0.14 65 0.16 56 0.18 51 0.19(fracture)
Case Study Calculate the Tensile Toughness Tensile toughness measures the total energy absorbed prior to fracture and is different from fracture toughness and impact toughness. Fracture toughness measures the resistance to fracture when a flaw (i.e. crack) is present in the material. Since it is nearly impossible and costly to manufacture materials with zero or near zero defects, fracture toughness is a major consideration for all structural materials. Impact toughness measures a materials ability to withstand an impact blow (i.e. high strain rates) and is particularly important in assessing the ductile-to-brittle transition behavior (more details later). Impact toughness is also commonly referred to as notch toughness. The tensile toughness can be estimated using the stress-strain curve by measuring the area under the curve (both the elastic and plastic regions). Tensile Toughness = f Stress, σ Ty- Ey Efracture ETS Ur Ey Efracture o de = U₁ + SETS o de + Sefracture o de Ey Ey o de =…
specimen of stainless steel having a diameter of 12.8mm and gauge lengh of A cylindrical the following: (6) Extend the table to include engincering strain and engineering stress and plot the Engineering stress-strain curve Determine the yield stress at 0.002 strain offset (i1) (in) Determine the Modulus of Elasticity What is the tensile strength of the Alloy? What is the ductility in percent elongation: What is the Modulus of Resilience? (iv) (v) (vi) ble 1. Load-Extension Test Data of Stainless Stee! LOAD (N) LENGTH(mm) 50.800 50.825 12700 25400 38100 50800 76200 89100 92700 102500 107800 119400 128300 50.851 50.876 0001 50.902 50.952 51.003 CCOn 12-8 51.054 51.181 51.308 51.562 51.816 149700- 52.832 159500- 53.848 160400 54.365 159500- 151500 124700 14. 54.864 55.880 56.642 1 000 05 Pcu/coer 0.00
A copper specimen subjected to the Brinell Hardness Test using hardened steel ball indenter of diameter 12 mm and the indentation diameter 3.87 mm is measured using an optical magnifying lens with a ruler. Draw the Brinell Hardness Test setup neatly and determine the force applied on the specimen. Take Brinell Hardness Number for copper as 807. Calculate: 1-Surface Area of Indentation (in mm2) 2-Applied Force (in N)
Question-7. Steady-state creep data taken for an alloy at a stress level of 160 MPa are given below. The stress exponent n for the alloy is 6.8. R is 8.3145 J/mol-K. Compute the steady-state creep rate at 1000 °C and a stress level of 68 MPa. Es (h-1) 6.8 × 10-5 T (°C) 800 8.6 x 10-3 900
Mechanical Engineering Consider two polycrystalline samples with grain size of 0.25 and 5 um. Cooling of the materials produces cracks due to the thermal expansion mismatch. The approximate dimensions are similar to the grain-boundary facets. Determine the tensile strength of the two materials if both have Kiç as 3.5 MN m0.3. Which sample would you use for your project that requires high strength? (geometric factor is unknown)
A material has a linear elastic perfectly plastic stress-strain. A cylindrical specimen of that material having an initial length of 35 mm and a tadius of 7 mm is pulled until it elongates 0.8mm. a. Calculate the stain and the corresponding stress at that elongation value. b. Afterward, the specimen is released to zero stress level, how does the final length of the specimen compare with its original length? How much plastic deformation remains if it exists?