phase diagram 1400Temperature (°C)12001000€ 8006004002000Cuα20x + liquid19.1a +BLiquid6040Composition (wt% Ag)Figure 161.180B+L97.3♡Temperature (°C)100%AgFigure 1 shows a Cu-Ag phase diagram. Analyze the phase analysis for 40 wt% Ag - 60 wt%Cu at 900 °C.

Answered: Figure 1 shows a Cu-Ag phase diagram.…

Engineering

Mechanical Engineering

Figure 1 shows a Cu-Ag phase diagram. Analyze the phase analysis for 40 wt% Ag - 60 wt% Cu at 900 °C.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Consider the phase diagram below. The three points A, B, and C are at concentrations of 26.4, 31.3, and 34 wt% Ni respectively. The ends of the tie line are at C1 = 25% wt% Ni and C2 = 35 wt% Ni. What are the weight fractions of the alpha phase at A and the L phase at B, as well as the alpha phase/L phase ratio at C? T(°C) 1300 L (liquid) 1200 20 A B C L + a C1 S liquidus L + a solidus a (solid) 50 wt% Ni a. Walpha=0.21; WL=0.33; Walpha/WL = 13.17 b. Walpha=0.09; WL=0.32; Walpha/WL = 15.00 c. Walpha=0.07; WL=0.46; Walpha/WL = 11.17 d. Walpha=0.14; WL=0.37; Walpha/WL = 9.00
Consider the phase diagram below. The three points A, B, and C are at concentrations of 27.8, 31.6, and 33.5 wt% Ni respectively. The ends of the tie line are at C1 = 25% wt% Ni and C2 = 35 wt% Ni. What are the weight fractions of the alpha phase at A and the L phase at B, as well as the alpha phase/L phase ratio at C? T(°C) 1300 1200 - L (liquid) 20 ABC L + a C1 30 S C2 liquidus 40 L + a solidus α (solid) a. Walpha=0.34; WL=0.29; Walpha/WL = 8.94 b. Walpha=0.23; WL=0.29; Walpha/WL = 8.85 c. Walpha=0.28; WL=0.34; Walpha/WL = 5.67 d. Walpha=0.19; WL=0.44; Walpha/WL = 7.56 50 wt% Ni
temperatrue (°C) 400 300 200 183 100 0 0 100% Pb 19 20 61.9 40 60 Weight percent tin Fox Ligund 80 97.5 100% Sn Figure 1 Figure 1 shows a Pb-Sn phase diagram. Analyze the phase analysis for a 60 wt% Pb - 40 wt% Sn at 200 °C.
Consider the phase diagram below. The three points A, B, and C are at concentrations of 27.3, 31.2, and 33.3 wt% Ni respectively. The ends of the tie line are at C1 = 25% wt% Ni and C2 = 35 wt% Ni. What are the weight fractions of the alpha phase at A and the L phase at B, as well as the alpha phase/L phase ratio at C? T(°C) 1300 1200 20 L (liquid) ABC L+a C1 Previous page 30 S liquidus L + a solidus α (solid) O a. Walpha=0.23; WL-0.38; Walpha/WL = 4.88 O b. Walpha=0.15; WL-0.47; Walpha/WL = 6.65 O c. Walpha=0.18; WL-0.33; Walpha/WL = 7.53 O d. Walpha=0.30; WL-0.34; Walpha/WL = 7.87 50 wt% Ni MacBook Pro Next page
Refer to the following phase diagram (not to scale!) for nitrogen : 33.5 1.00 atm 0.127 63.1 63.2 77.4 126.0 T Kolvin At a pressure of 1 atm, the temperature 63.2 K is called the The normal boiling point for Ng is at The triple point pressure for Nz is ]of N2 - K atm The critical pressure for Ng is 33.5 atm. At temperatures above 126 K and pressures above 33.5 atm, Ny is a Nz is a[ Nz is a N2 is a |at 26.4 atm and 57.5 K. |at 1.00 atm and 75.1 K. at 0.127 atm and 83.0 K.
Consider the phase diagram below. The three points A, B, and C are at concentrations of 27, 31.9, and 33.8 wt% Ni respectively. The ends of the tie line are at C1 = 25% wt% Ni and C2 = 35 wt% Ni. What are the weight fractions of the alpha phase at A and the L phase at B, as well as the alpha phase/L phase ratio at C? T(°C) 1300-L (liquid) 1200 20 ABC L + a C1 30 S C2 liquidus 40 L + a solidus α (solid). O a. Walpha=0.12; WL=0.41; Walpha/WL = 9.41 O b. Walpha=0.27; WL-0.26; Walpha/WL = 11.11 O c. Walpha=0.15; WL-0.26; Walpha/WL = 11.80 Od. Walpha=0.20; WL-0.31; Walpha/WL = 7.33 50 wt% Ni
Figure 1 shows a binary phase diagram of elements A and B. Determine the phases present, composition, and amount of each phase at 215 °C. T(°C) 300+ 215 200+ 100+ 0 A L+a 1720 Ca L (liquid) 183°C a + ß 40 46 60 Co CL wt% 80 +B 100 B
Use the Cu-Ag Phase Diagram below to answer the following questions Composition (at% Ag) 20 40 60 80 100 2200 1200 A 2000 Liquidus 1000 Liquid 1800 Solidus C F a +L 1600 * 800 779 C (T) B+L E G 91.2 (Ceg 8.0 71.9 1400 (Cg). 1200 600 Solvus 1000 a +B 800 400 600 200 o 400 100 20 40 60 80 (Cu) Composition (wt% Ag) (Ag) Temperature ("C) Temperature ("F)
b) Figure 1 shows a Cu-Ag phase diagram. Calculate the phase analysis for 50% Ag-50% Cu at 800 °C. Temperature (°C) 1200 1000 800 600 400 200 ( C (Cu) B 8.0 (C₂g) -Solidus Solvus 20 20 a + L Composition (at% Ag) 40 -Liquidus 779°C (TE) a + B 40 Liquid 60 Composition (wt% Ag) 60 71.9 (CE) 80 80 B+L 91.2 (CBg) G to 100 2200 2000 1800 F 1600 1400 1200 1000 800 600 400 100 Temperature (°F)
Temperature (°C) C2. The following questions refer to the phase diagram below: Composition (at% C) 1600 1538°C 1493°C 5 1400 1394°C Y+L 10 15 L 20 25 2500 1200 1147°C 2.14 y, Austenite 4.30 2000 1000 912°C 800 a Y 0.76 600 0.022 a, Ferrite 400 0 2 a+ Fe3C 3 4 y+ Fe3C 727°C 1500 Cementite (Fe3C). 1000 (Fe) Composition (wt% C) For a 8 kg steel alloy containing 1.75 wt % C, answer the following: What phases are present at 800°C and at 1150°C? (a) (b) i) What is the proeutectoid phase for this alloy? 6 6.70 ii) For this specific composition, what is the approximate temperature range that the proeutectoid phase would be formed in? (c) Just above the eutectoid temperature, i) What is the approximate composition of each phase? ii) How many kg of each phase is present? Temperature (°F) 4
Temperature (°C) C2. Continued. The following questions refer to the phase diagram below: 5 Composition (at% C) 10 15 20 25 0 1600 1538°C 1493°C 1400 1394°C Y+L 1200 2.14 y. Austenite 1000 912°C 800 a Y 0.76 600 0.022 a, Ferrite 1147°C a+ FezC L 2500 4.30 2000 y+ FegC 727°C 1500 Cementite (Fe3C). 1000 400 (Fe) 2 3 Composition (wt% C) 4 5 6 6.70 For a 8 kg steel alloy containing 1.75 wt % C, answer the following: c) Just below the eutectoid temperature, how many kg of pearlite is formed (if any)? (d) Just below the eutectoid temperature, how many total kg of Fe3C are formed (if any)? Temperature (°F) 5
Consider Cu - Ag Phase diagram below: 1200 A -Liquidus 1000 Liquid -Solidus 779°C (TE) 800 Temperature (°C) 600 400 a C 200 0 B 8.0 (Cag) Solvus a +L a + ß E 71.9 (CE) B+L 91.2 (CBE) B H 1 1 1 1 1 { ( L 20 40 60 80 100 (Cu) Composition (wt% Ag) (Ag) Consider 71.9% Ag-28.1% Cu, which is cooled below 779°C. What is the composition of the phases present just below 779°C and give the amount of beta phase present